Regus, Matthias, Kuhn, Gerhard, Mankovsky, Sergej, Ebert, Hubert and Bensch, Wolfgang (2012) Investigations of the crystallization mechanism of CrSb and CrSb2 multilayered films using in-situ X-ray diffraction and in-situ X-ray reflectometry. Journal of Solid State Chemistry, 196 . pp. 100-109. DOI 10.1016/j.jssc.2012.06.046.

Full text not available from this repository.

Abstract

Chromium and antimony multilayered films with variable elemental layer thickness were deposited on (1 0 0)-Si substrate cooled with liquid nitrogen. The stoichiometry of the films was adjusted to Cr:Sb=1:1 and 1:2. The thickness of Cr–Sb repeating units of these multifilms was varied between 11.4 and 102.5 Å. Satellite maxima in the X-ray reflectivity curves observed for films in the as-deposited state demonstrate an alternating stacking of the evaporated elements. The reactivity of the superlattice reactants was investigated with temperature dependent in-situ X-ray diffractometry and X-ray reflectometry. The crystallization temperature of CrSb depends on the double-layer thickness and is about 90 °C for a Cr:Sb ratio of 1:1 and double-layer thickness of 53.7 Å where nucleation and crystal formation occurs at the element interfaces, while for a thin double-layer thickness (11.4 Å) first interdiffusion of the elements occurs before crystallization starts, i.e., an amorphous intermediate is formed prior to crystallization of CrSb. A decomposition reaction into CrSb2 occurs at about 230 °C, and up to about 575 °C, CrSb, CrSb2 and amorphous Cr coexist. For the ratio Cr:Sb=1:2 and a thin double-layer thickness prior to crystallization of CrSb2 nano-sized crystallites with a composition near CrSb2 nucleate and grow. These crystallites are then successively transformed in long-range ordered crystals exhibiting a pronounced preferred orientation. For films with a thicker repeat unit first formation of CrSb is observed which then reacts with elemental Sb yielding crystalline CrSb2. An activation energy for interdiffusion of Cr and Sb of about 1.8 eV is estimated for a film with Cr:Sb=1:1 exhibiting a double-layer thickness of about 53.7 Å and an energy for crystal growth of about 1.1 eV. For the film with the thinner double-layer thickness of 11.4 Å a lower value of the activation energy for interdiffusion is obtained. For CrSb2 the energy for crystal growth is about 3.0 eV being significantly larger than for CrSb. Specific resistivity and Hall coefficient measurements were performed for crystalline CrSb and CrSb2 films. The temperature-dependent resistivity measurement exhibits a metallic behavior for CrSb and semi-conducting properties for CrSb2

Document Type:	Article
Keywords:	Thin films, In-situ X-ray diffraction, In-situ X-ray reflectometry, Chemical reactivity, Crystallization and growth, Chromium antimonides
Research affiliation:	Kiel University Kiel University > Kiel Marine Science OceanRep > The Future Ocean - Cluster of Excellence
Refereed:	Yes
Open Access Journal?:	No
Publisher:	Elsevier
Projects:	Future Ocean
Date Deposited:	12 Jun 2018 10:31
Last Modified:	23 Sep 2019 20:13
URI:	https://oceanrep.geomar.de/id/eprint/43336

Actions (login required)

View Item